Effect of laser-assisted retrograde cavity preparation on push-out-bond-strength of mineral trioxide aggregate and calcium-enriched-mixture-cement
Bahadır, H.S., Türkyilmaz, A., Bayraktar, Y. & Çelik, Ç.Brazilian Dental Science, 2022;25(1), p.e2736.
Background:
This study aimed to determine the push-out-bond-strength(PBS) of mineral trioxide aggregate (BIOMTA+) and calcium-enriched-mixture-cement (CEM) in retrograde cavities prepared using Er: YAG laser and stainless-steel bur.
Material and Methods:
The root canals of 60 extracted single-rooted human teeth were prepared, filled and their apical portion of 3-mm were resected using a diamond bur and randomly divided into four groups according to technique of retrograde preparation and filling material as follows(n=15): Group1: bur/ BIOMTA+,Group2: bur/ CEM, Group3: Er:YAG laser/ BIOMTA+, Group4: Er:YAG laser/ CEM. PBS test were performed to specimens and failure modes were evaluated. The data were statistically analyzed with ANOVA, Post-Hoc Tukey and t tests (p< 0.05).
Results:
CEM was exhibited higher than bond strength compared to BIOMTA+ in retrograde cavity prepared using laser (p= 0.021) and BIOMTA+ in retrograde cavity prepared using bur was exhibited higher than bond strength compared to in retrograde cavities prepared using laser (p= 0.024). Failure modes were dominantly cohesive in all groups tested and one representative specimen each failure mode was examined in SEM and the general characteristics of the failure modes were confirmed.
Conclusion:
With in the limitations of the present study, when used CEM, Er: YAG laser-assisted retrograde cavity preparation positively affected the bond strength values compared to BIO MTA+. Considering its optimal adhesion, the calcium-enriched-mixture-cement (CEM) might be a good option as a filling material in retrograde cavities in clinical use.